Tiwb Dur Di-staen Duplex ASTM A789

1. Safon: ASTM A789, ASME SA 789
2. Maint tiwb di-dor: 1/2" i 8"
3. Maint Tiwb Wedi'i Weldio: 6" i 24"
4. Diamedr Allanol: 6.0mm-630mm
5. Trwch Wal: 1mm i 50mm

Anfon ymchwiliad

Cyflwyniad Cynnyrch

Tiwb dur di-staen deublyg ASTM A789,yn cynnwys tua 50% ferrite a 50% austenite. Mae gan bibell ASTM A789 well ymwrthedd cyrydiad straen mewn datrysiad clorid niwtral a H2S na 304L, dur di-staen austenitig 316L. Mae'r bibell hon yn arbennig o addas ar gyfer yr ystod tymheredd o -50 gradd F/+600 gradd F. Rydym yn gyflenwr 2507 gyda 15+ o brofiad allforio. Gallwn ddarparu pibellau di-dor a phibellau wedi'u weldio, gan gynnwys diamedrau bach i ddiamedrau mawr. Cysylltwch â ni am ragor o wybodaeth a dyfynbrisiau am ddim!

Safon tiwb dur dwplecs ASTM A789:

ASTM A789: Manyleb Safonol ar gyfer Tiwbiau Dur Di-staen Ferritig / Austenitig Wedi'i Weldio ar gyfer Gwasanaeth Cyffredinol

Graddau: S31803, S32205, S32750, S32760, S32550

ASME B36.19: Manyleb ar gyfer Pibellau Dur Di-staen

ASTM A789 Stainless Steel Tube Suppliers

Manylebau Tiwb Dur Di-staen Duplex ASTM A789

Safonol	ASTM A789/A789M, ASME SA789
Pibell ddi-dor a Maint Tiwb	1/2" i 8" MEWN
Pibell wedi'i Weldio a Maint Tiwb	6" i 24" MEWN
Diamedr Allanol	6.0-630}mm
Atodlenni	5s, 10s, 20% 2C 40s, 40% 2C 60% 2C 80s, 80% 2C 100% 2C 120% 2C 140% 2C XXH.
Trwch Wal	1mm i 50mm
Gorffen	Wedi'i sgleinio, AP (Annealed & Pickled), BA (Bright & Annealed), MF
Ffurf	Tiwbiau Crwn, Sgwâr, Hirsgwar, Hydrolig, Syth neu 'U' Etc.
Hyd	Ar Hap Sengl, Hap Dwbl, a Hyd Torri.
Diwedd	Diwedd Plaen, Diwedd Beveled, Treaded

Goddefgarwch Dimensiynol Safonol ASTM A789

ASTM A789	Maint, Tu Allan Diamedr, [mm]	Amrywiadau Caniataol, yn OD	Amrywiadau Caniataol, yn WT	Amrywiadau Caniataol, yn Hyd	Tiwb Wal Tenau
	D＜12.7	�% B1% 7B{0}}.13mm	±15%	3mm	...
	12.7-38.1	�% B1% 7B{0}}.13mm	±10%	3mm	WT<1.6mm
	38.1-88.9	�% B1% 7b{0}}.25mm	±10%	5mm	WT<2.4mm
	88.9-139.7	�% B1% 7B{0}}.38mm	±10%	5mm	WT<3.8mm
	139.7-203.2	�% B1% 7B{0}}.76mm	±10%	5mm	WT<3.8mm

Cyfansoddiad Cemegol Tiwb Dur Di-staen ASTM A789 Duplex

Gradd	C Llai na neu'n hafal i	Mn Llai na neu hafal i	P Llai na neu hafal i	S Llai na neu'n hafal i	Si Llai na neu hafal i	Ni	Cr	Mo	N	Cu
S31803	0.03	2.00	0.03	0.02	1.00	4.5–6.5	21.0–23.0	2.5–3.5	0.08–0.20	-
S32205	0.03	2.00	0.03	0.02	1.00	4.5–6.5	22.0–23.0	3.0–3.5	0.14–0.20	-
S32750	0.03	1.20	0.035	0.02	0.80	6.0-8.0	24.0-26.0	3.0-5.0	0.24-0.32	0.5
S32760	0.05	1.00	0.03	0.01	1.00	6.0-8.0	24.0-26.0	3.0-4.0	0.20-0.30	0.50–1.00

Priodweddau Mecanyddol Materol ASTM A789

Priodweddau mecanyddol	Tynnol, mun, ksi[MPa]	Cnwd, min, ksi[MPa]	Elongation, %(mun)	Caledwch, HB (uchafswm)
S31803	90 [620]	65 [450]	25	290
S32205	95 [655]	65 [450]	25	290
S32750	116 [800]	80 [550]	15	300
S32760	109 [750]	80 [550]	25	300

Triniaeth Gwres Tiwb ASTM A789

Dynodiad UNS	Gradd tymheredd F [ gradd ]	Chwalu
S31803	1870-2010℉(1020-1100 gradd )	Oeri cyflym mewn aer neu ddŵr
S32205	1870-2010℉(1020-1100 gradd )	Oeri cyflym mewn aer neu ddŵr
S32750	1880-2060℉(1025-1125 gradd )	Oeri cyflym mewn aer neu ddŵr
S32760	2010-2085℉(1100-1140 gradd )	Oeri cyflym mewn aer neu ddŵr

Priodweddau Ffisegol UNS S31803 a S32205

Gradd	Dwysedd (kg/m3)	Elastig modwlws (GPa)	Cymedrig Cyd-eff Thermol Ehangu (μm/m/ gradd)			Thermol Dargludedd (W/mK)		Penodol Gwres 0-100 gradd ( J/kg.K)	Trydanol Gwrthedd (nΩ.m)

			0-100 gradd	0-315 gradd	0-538 gradd	ar 100 gradd	ar 500 gradd
2205	782	190	13.7	14.2	-	19	-	418	850